Dam & Fill and Glob-Top

PROTAVIC’s Dam & Fill reduces warping and provides superior protection during torsion and bending tests undergone by micro-connectors during validation.


PROTAVIC’s Glob-Top is intended for smaller chips.

PROTAVIC’s Dam & Fill and Glob-Top ranges offer different curing options for protecting smart card micromodules:

  • UV curing allows for quicker processing in mass production
  • Thermal curing allows for low coefficients of thermal expansion (CTE) and high glass transition temperatures (Tg).

Some examples are listed in the table below.

Technical description

Name名称

Color颜色

Chemistry

Density

Viescosity at 25°C(mPa.s)

Glass transition temperature(TG)

CTE(ppm/°C)

Shore hardness

Thermal conductivity(W/(m.K))

Use

Dielectric strength(kV/mm)

Open time

Polymerization/Crosslinking

Storage

PROTAVIC® PNE 90300

Off-white

Epoxy

1.4

16000

24°C

140

D55

-

Dam

-

-

30 sec at 120 mW/cm² UV A

6 months at 5°C

PROTAVIC® PNE 90301

Off-white

Epoxy

1.47

2600

50°C

100

D80

-

Fill

-

-

30 sec at 120mW/cm² UV A

6 months at 5°C

PROTAVIC® PNE 90397

Off-white

Epoxy

1.7

7500

100°C

30

D92

-

Globtop

-

-

30 sec at 120mW/cm² UV A

1 year at 5°C

PROTAVIC® PNE 90300

Off-white

Epoxy

Chemistry

1.4

Density

16000

Viescosity at 25°C(mPa.s)

24°C

Glass transition temperature(TG)

140

CTE(ppm/°C)

D55

Shore hardness

-

Thermal conductivity(W/(m.K))

Dam

Use

-

Dielectric strength(kV/mm)

-

Open time

30 sec at 120 mW/cm² UV A

Polymerization/Crosslinking

6 months at 5°C

Storage

PROTAVIC® PNE 90301

Off-white

Epoxy

Chemistry

1.47

Density

2600

Viescosity at 25°C(mPa.s)

50°C

Glass transition temperature(TG)

100

CTE(ppm/°C)

D80

Shore hardness

-

Thermal conductivity(W/(m.K))

Fill

Use

-

Dielectric strength(kV/mm)

-

Open time

30 sec at 120mW/cm² UV A

Polymerization/Crosslinking

6 months at 5°C

Storage

PROTAVIC® PNE 90397

Off-white

Epoxy

Chemistry

1.7

Density

7500

Viescosity at 25°C(mPa.s)

100°C

Glass transition temperature(TG)

30

CTE(ppm/°C)

D92

Shore hardness

-

Thermal conductivity(W/(m.K))

Globtop

Use

-

Dielectric strength(kV/mm)

-

Open time

30 sec at 120mW/cm² UV A

Polymerization/Crosslinking

1 year at 5°C

Storage