FERRITE BONDING
PROTAVIC® heat cure epoxy adhesives provide excellent adhesion to ferrites, PCBs and many metal interfaces. Its great stability ensures the module works well under high temp conditions.
PROTAVIC® adhesives are adaptable to needle dispensing as well as jetting. The ideal rheology makes them able to wet the bonding interface and achieve 0 gap between ferrites after curing.
PROTAVIC® adhesives are also designed to achieve a customerized gap size between 0um~600um.
Technical description
Name名称
Color颜色
Chemistry
Density
Viescosity at 25°C(mPa.s)
Glass transition temperature(TG)
CTE(ppm/°C)
Shore hardness
Use
Open time
Polymerization/Crosslinking
Storage
PROTAVIC® ANE 26144
Amber
Epoxy
1.1
3700
110°C
69
D88
Ferrite Bonding
2 days
15 min at 150°C
1 year at RT
PROTAVIC® ANE 26149
Amber
Epoxy
1.2
400
125°C
76
D88
Ferrite Bonding
24 hours
5 min at 150°C
1 year at RT
PROTAVIC® ATE 10120
Grey
Epoxy
1.6
25000
80°C
50
-
Gap Fill
> 5 days
30 min at 150°C
6 months at -20°C
PROTAVIC® ANE 26144
Amber
Epoxy
Chemistry1.1
Density3700
Viescosity at 25°C(mPa.s)110°C
Glass transition temperature(TG)69
CTE(ppm/°C)D88
Shore hardnessFerrite Bonding
Use2 days
Open time15 min at 150°C
Polymerization/Crosslinking1 year at RT
StoragePROTAVIC® ANE 26149
Amber
Epoxy
Chemistry1.2
Density400
Viescosity at 25°C(mPa.s)125°C
Glass transition temperature(TG)76
CTE(ppm/°C)D88
Shore hardnessFerrite Bonding
Use24 hours
Open time5 min at 150°C
Polymerization/Crosslinking1 year at RT
StoragePROTAVIC® ATE 10120
Grey
Epoxy
Chemistry1.6
Density25000
Viescosity at 25°C(mPa.s)80°C
Glass transition temperature(TG)50
CTE(ppm/°C)-
Shore hardnessGap Fill
Use> 5 days
Open time30 min at 150°C
Polymerization/Crosslinking6 months at -20°C
Storage