THERMAL GEL

As liquid thermal management materials, gels are designed to help customer effectively manage heat in electronic applications, improving device performance and overall reliability. The liquid forms mean they are highly conformable, and can be utilized across many different types of assembly.  

PROTAVIC® high TC gels minimize stress, and offer great flexibility, highly conformable gap-fillability and good heat conduction between diverse interfaces.

Technical description

Name名称

Color颜色

Chemistry

Density

Viescosity at 25°C(mPa.s)

Shore hardness

Thermal conductivity(W/(m.K))

Working Temp

UL-Certified

Open time

Polymerization/Crosslinking

Storage

Dielectric constant (120Hz)

PROTAVIC® PTS 46500-25

Pink

Silicone

3.0

Paste

Shore00/65

2.5

-65°C~200°C

94 V0

120 min

24 hours at 25°C

6 months at RT

4.7

PROTAVIC® PTS 46500-40

Pink

Silicone

3.0

Paste

Shore00/65

4.0

-65°C~200°C

94 V0

-65°C~200°C

24 hours at 25°C

6 months at RT

4.7

PROTAVIC® PTS 46500-70

Pink

Silicone

3.0

Paste

Shore00/65

7.0

-65°C~200°C

94 V0

120 min

24 hours at 25°C

6 months at RT

4.7

PROTAVIC® PTS 46500-25

Pink

Silicone

Chemistry

3.0

Density

Paste

Viescosity at 25°C(mPa.s)

Shore00/65

Shore hardness

2.5

Thermal conductivity(W/(m.K))

-65°C~200°C

Working Temp

94 V0

UL-Certified

120 min

Open time

24 hours at 25°C

Polymerization/Crosslinking

6 months at RT

Storage

4.7

Dielectric constant (120Hz)

PROTAVIC® PTS 46500-40

Pink

Silicone

Chemistry

3.0

Density

Paste

Viescosity at 25°C(mPa.s)

Shore00/65

Shore hardness

4.0

Thermal conductivity(W/(m.K))

-65°C~200°C

Working Temp

94 V0

UL-Certified

-65°C~200°C

Open time

24 hours at 25°C

Polymerization/Crosslinking

6 months at RT

Storage

4.7

Dielectric constant (120Hz)

PROTAVIC® PTS 46500-70

Pink

Silicone

Chemistry

3.0

Density

Paste

Viescosity at 25°C(mPa.s)

Shore00/65

Shore hardness

7.0

Thermal conductivity(W/(m.K))

-65°C~200°C

Working Temp

94 V0

UL-Certified

120 min

Open time

24 hours at 25°C

Polymerization/Crosslinking

6 months at RT

Storage

4.7

Dielectric constant (120Hz)